Table 1 Volumetric parameters (mean ± standard deviation) of the microCT morphological analysis for scaffolds coated with TiO2 (n = 6)

From: Enhanced Osteoblast Differentiation on Scaffolds Coated with TiO2 Compared to SiO2 and CaP Coatings

Parameter Unit Mean SD
Porosity % 91.66 1.82
Surface area-to-volume ratio l/mm 54.57 6.84
Pore size μm 440.36 12.84
Strut thickness μm 64.73 5.93
Intersection surface mm2 9.54 2.24
Interconnectivity <160 μm % 95.81 1.09